Properties:   High reactive, low viscosity pre-accelerated, fast cure rates, fast wet-out, high quality smooth surface, high filler acceptance
Applications:  Automotive, building and construction industry
MODIFICATIONS : |
Pre-accelerated (A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
Ortho |
140-160 ( #2/60 rpm @20 °C) |
5-8 (@20 °C 2 mL % 60 MEK-P) |
 |
 |
Properties:   Medium reactive, low viscosity pre-accelerated, fast cure rates, moderate exotherm, economic, high filler acceptance
Applications:  Automotive and construction industry
MODIFICATIONS : |
Pre-accelerated (A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
Ortho |
250-300 ( #2/50 rpm @20 °C) |
5-6 (@20 °C 2 mL % 60 MEK-P) |
 |
 |
Properties:   Medium reactive, low viscosity, thixotrophic, pre-accelerated, low styrene emission (LSE), ideal resin for large composite parts with vertical surfaces
Applications:  Automotive and construction industry
MODIFICATIONS : |
Thixotropic(T), Pre-accelerated(A), Düşük Stren Emisyonunlu(LSE) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
Ortho Tix |
500-600 (#2/20 rpm @25°C) |
6-7 (@20 °C 2 mL % 60 MEK-P) |
 |
 |
Properties:   Medium reactive, low viscosity, low volumetric shrinkage, high mechanical properties, high filler
acceptance
Applications:  Automotive and construction industry
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
150-250 (#3/50 rpm @23 °C) |
14-16 (@23 °C 1 mL % 60 MEK-P) |
 |
 |
Properties:   High reactive, pre-accelerated, low viscosity, good mechanical strength, anti-corrosion toughness,
HDT and elongation, fast hardness
Applications:  Automotive and construction industry
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
İso |
230-260 (#3/50 rpm @25 °C) |
7-9 (@25 °C 2.0 mL % 60 MEK-P) |
 |
 |