Hand Lay-up & Spray-up

Hand Lay-up & Spray-up

Hand lay-up is the most common and least expensive open-molding method because it requires the least amount of equipment. Fiber reinforcements are placed by hand in a mold and resin is applied with a brush or roller. This process is used to make both large and small items, including boats, storage tanks, tubs and showers.
Spray-up, or chopping, is an open mold method similar to hand lay-up in its suitability for making boats, tanks, transportation components, and tub/shower units in a large variety of shapes and sizes.

PRE-03 TA GENERAL PURPOSE POLYESTER RESIN

Properties:   Resilient, thixotropic, low viscosity, pre-accelerated, fast wet-out of chopped glass stands and easy rolling, high thixotropic index, fast trim and cure times, non-air-inhibited

Applications:  Moulding of glass reinforced parts, using alumina hydrate as an extender and fire retardant

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 250-400 (#2/20 rpm @25 °C) 15-20 (@25 °C 1 mL % 50 MEK-P) TDS MSDS
PRE-60 GENERAL PURPOSE POLYESTER RESIN

Properties:   Low viscosity, high reactive, fast curing and high filler of calcium carbonate, aluminium hydroxide, marble powder acceptance for casting and low volumetric shrinkage

Applications:  GRP, FRP and clear casting

MODIFICATIONS : -
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho 180-200 (#2/60 rpm @25 °C) 25-30 (@25 °C 0.15 mL Co %6, 1 mL % 60 MEK-P) TDS MSDS
PRE-63 TAB GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, medium reactive, pre-accelerated with blue indicator, medium viscosity, good fiber wet-out, low shrinkage, high filler acceptance, water resistant

Applications:  GRP, FRP and clear casting

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 500-600 (#2/20 rpm @25 °C) 8-10 (@25 °C 1 mL % 60 MEK-P) TDS MSDS
PRE-63 TAB HV GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, high viscosity, pre-accelerated with blue indicator, high filler acceptance, excellent wetting for fiber, good heat resistance, easy rolling due to high viscosity

Applications:  GRP, FRP and clear casting

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), High Viscosity (HV)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 900-1000 (#2/20 rpm @23 °C) 10-15 (@25 °C 1 mL % 60 MEK-P) TDS MSDS
PRE-6300 TAB GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, medium viscosity, medium reactive, pre-accelerated with blue indicator, thixotropic property allows application on vertical parts without the risk of sagging or drainage, rapid wetting, good and quick cure

Applications:  Fabrication of FRP marine craft

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 290-340 (#3/100 rpm @23°C) 18-30 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-6301 TAB LSE GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, low viscosity, low styrene emission (LSE), fast cure

Applications:  General purpose laminating

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 200-260 (#3/100 rpm @23°C) 12-16 (@25 °C 1.5 mL % 50 MEK-P) TDS MSDS
PRE-6302 TAB GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, medium viscosity, medium-fast cure

Applications:  General purpose laminating

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 290-340 (#3/100 rpm @23°C) 19-21 (@25 °C 1.5 mL % 50 MEK-P) TDS MSDS
PRE-6303 TAB LSE GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, medium viscosity, low styrene emission (LSE), its thixotropic structure prevents drainage when it's used on vertical surface with chopped stand mat

Applications:  General purpose laminating

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 290-340 (#3/100 rpm @23°C) 19-21 (@25 °C 1.5 mL % 50 MEK-P) TDS MSDS
PRE-6304 TAB LSE GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, low viscosity, low styrene emission (LSE), good fiber wet-out, medium cure, high filler acceptance, water resistant

Applications:  Calcium carbonate filled lamination

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 170-210 (#3/100 rpm @25°C) 15-20 (@25 °C 0.63 mL % 50 MEK-P) TDS MSDS
PRE-6305 TAB LSE GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, low viscosity, medium cure, good fiber wet-out and low odour

Applications:  Suitable for indoor applications

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 200-250 (#3/100 rpm @23°C) 22-25 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-6306 TAB GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-acceleratedwith blue indicator, medium viscosity, medium cure, high filler acceptance, excellent wetting for fiber, good heat resistance, easy rolling

Applications:  FRP lamination

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 320-360 (#3/100 rpm @25°C) 18-25 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-6307 TAB LSE GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-acceleratedwith blue indicator, medium viscosity, medium cure, low shrinkage, low odour, good fiber wet-out

Applications:  FRP lamination

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 320-360 (#3/100 rpm @25°C) 18-25 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-6308 TAB LSE GENERAL PURPOSE POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, medium viscosity, low styrene emission (LSE), excellent fiber wet-out

Applications:  Large FRP boat manufacturing

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 320-360 (#3/100 rpm @25°C) 18-25 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-6320 GENERAL PURPOSE POLYESTER RESIN

Properties:   Medium reactive, medium viscosity, easy fiber wet-out, medium-fast cure

Applications:  FRP, GRP and clear casting applications, manufacture big size composite parts

MODIFICATIONS : -
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho 450-500 ( #2/20 rpm @25°C) 7-9 (@25 °C 0.25 mL Co %6, 2 mL % 60 MEK-P ) TDS MSDS
PRE-6321 GENERAL PURPOSE POLYESTER RESIN

Properties:   High reactive, medium viscosity, transparent, low volume deformation, easy fiber wet-out

Applications:  Fast trim and serial production of FRP, GRP

MODIFICATIONS : -
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho 350-400 ( #2/20 rpm @25°C) 4-7 (@25 °C 0.25 mL Co %6, 2 mL % 60 MEK-P ) TDS MSDS
PRE-5040 TAB LSE LOW STYRENE EMISSION POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, low styrene emission (LSE), high heat distortion, excellent fiber wetting and rolling, low odour

Applications:  GRP-FRP products with enhanced mechanical and therma properties

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 450-600 ( #2/20 rpm @25°C) 23-31 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-7210 TAB LSE CORROSION RESISTANT ISOPHTHALIC /NPG POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated with blue indicator, medium viscosity excellent fiber wet-out, high corrosion resistant

Applications:  GRP-FRP products where high gloss and corrosion resistant are required

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Blue indicator (B), Low Styrene Emission(LSE)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
İso/NPG Tix 450-750 ( #2/20 rpm @23°C) 25-35 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
PRE-52 TA GRP TYPE ACRYLIC-ABS BACKING POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated, low viscosity, white, high filler acceptance, excellent adhesion to acrylic and ABS sheet, easy fiber wet-out, comparatively light, durable and economical

Applications:  Acrylic-ABS backing applications

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 180-220 (#3/50 rpm @25°C) 15-25 (@20 °C 1 mL % 60 MEK-P) TDS MSDS
PRE-52 TAD GRP TYPE ACRYLIC-ABS BACKING POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated, filled, low viscosity, white, high filler acceptance, excellent adhesion to acrylic and ABS sheet, easy fiber wet-out, comparatively light, durable and economical

Applications:  Acrylic-ABS backing applications

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Filled (D)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 2000-3000 (#3/20 rpm @25°C) 9-11 (@25 °C 1.5 mL % 60 MEK-P) TDS MSDS
PRE-52 TA LS GRP TYPE ACRYLIC-ABS BACKING POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated, low viscosity, white, low shrinkage (LS), high filling capacity, excellent adhesion to acrylic and ABS sheet, rapid fiber wetting, UV durable

Applications:  Acrylic-ABS backing applications

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A), Low Shirinkage(LS)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 180-220 (#3/50 rpm @25°C) 8-12 (@20 °C 1 mL % 60 MEK-P) TDS MSDS
PRE-510 TA GRP TYPE ACRYLIC-ABS BACKING POLYESTER RESIN

Properties:   Thixotropic, pre-accelerated, low viscosity, medium cure, rigid, high gloss, UV durable, high filler acceptance

Applications:  Acrylic-ABS backing applications

MODIFICATIONS : Thixotropic(T), Pre-accelerated(A)
TYPE VISCOSITY(cPS) GELTIME(MIN.) TDS MSDS
Ortho Tix 100-200 (#3/50 rpm @25°C) 14-18 (@25 °C 1.25 mL % 50 MEK-P) TDS MSDS
Modification Codes
T Thixotropic (no sagging)   LS Low Shrinkage
A Cobalt preaccelerated   HV High Viscosity
B Blue Indicator   LV Low Viscosity
D Filled   L UV light stabilized
FR Flame retardant   FT Brush or Roller Application
LSE Low Styrene Emission   TT Spray Application
Amine pre-accelerated   Color White or custom color options

Packages
You can choose any package type or you can contact to our sales department for information about container options.