Properties:   Special DCPD structure, thixotropic, pre-accelerated with blue indicator, low shrinkage, excellent fiber wet-out, low peak exotherm
Applications:  High surface quality composite parts
MODIFICATIONS : |
Thixotropic(T), Pre-accelerated(A), Blue indicator (B) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD Tix |
350-550 (#2/20 rpm @23°C) |
22-26 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   Special DCPD structure, pure, thixotropic, pre-accelerated with blue indicator, low shrinkage, excellent fiber wet-out, low peak exotherm
Applications:  High surface quality composite parts
MODIFICATIONS : |
Thixotropic(T), Pre-accelerated(A), Blue indicator (B) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD Tix |
400-500 (#3/60 rpm @23°C) |
20-25 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   Special DCPD structure, hybrid, thixotropic, pre-accelerated with blue indicator, low shrinkage, excellent fiber wet-out, low peak exotherm
Applications:  High surface quality composite parts
MODIFICATIONS : |
Thixotropic(T), Pre-accelerated(A), Blue indicator (B) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD Tix |
400-500 (#3/60 rpm @23°C) |
20-25 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based, pre-accelerated, medium rectivity, low shrinkage, low peak exhotherm, low styren emission
Applications:  High surface quality composite parts
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD Tix |
200-300 (#2/100 rpm @23°C) |
9-10 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based, hybrid, pre-accelerated, medium rectivity, low shrinkage, low peak exhotherm, low styren emission
Applications:  High surface quality composite parts
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/100 rpm @23°C) |
9-10 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based, pre-accelerated, medium rectivity, low shrinkage, low peak exhotherm, low styren emission
Applications:  High surface quality composite parts
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/100 rpm @23°C) |
43-45 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based, pre-accelerated, medium rectivity, low shrinkage, low peak exhotherm, low styren emission
Applications:  High surface quality composite parts
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/100 rpm @23°C) |
43-45 (@25 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based polyester resin, high mechanical properties, low shrinkage, high filler capacity, low viscosity
Applications:  High surface quality composite parts, automotive industry, construction industry
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/100 rpm @23°C) |
13-17 (@25 °C; 1 mL %1 Co; 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based polyester resin, hybrid, high mechanical properties, low shrinkage, high filler capacity, low viscosity
Applications:  High surface quality composite parts, automotive industry, construction industry
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/100 rpm @23°C) |
13-17 (@25 °C; 1 mL %1 Co; 2 mL % 50 MEK-P) |
 |
 |
Properties:   Special DCPD structure, pure, thixotropic, pre-accelerated with blue indicator, low shrinkage, excellent fiber wet-out, low peak exotherm
Applications:  High surface quality composite parts
MODIFICATIONS : |
Thixotropic(T), Pre-accelerated(A), Blue indicator (B) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD Tix |
400-500 (#3/60 rpm @23°C) |
17-20 (@25 °C; 1 mL % 60 MEK-P) |
 |
 |
Properties:   Special DCPD structure, hybrid, thixotropic, pre-accelerated with blue indicator, low shrinkage, excellent fiber wet-out, low peak exotherm
Applications:  High surface quality composite parts
MODIFICATIONS : |
Thixotropic(T), Pre-accelerated(A), Blue indicator (B) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD Tix |
400-500 (#3/60 rpm @23°C) |
17-20 (@25 °C; 1 mL % 60 MEK-P) |
 |
 |
Properties:   DCPD based, pre-accelerated, medium rectivity, low shrinkage, low peak exhotherm, low styren emission
Applications:  For artificial marble slabs production
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/20 rpm @25°C) |
16-20 (@20 °C 2 mL % 50 MEK-P) |
 |
 |
Properties:   DCPD based, hybrid, pre-accelerated, medium rectivity, low shrinkage, low peak exhotherm, low styren emission
Applications:  For artificial marble slabs production
MODIFICATIONS : |
Pre-accelerated(A) |
TYPE |
VISCOSITY(cPS) |
GELTIME(MIN.) |
TDS |
MSDS |
DCPD |
200-300 (#2/20 rpm @25°C) |
16-20 (@20 °C 2 mL % 50 MEK-P) |
 |
 |